Selelekela
Cristobalite ke mofuta o tlase oa SiO2 homomorphous variant, mme sebaka sa eona sa botsitso sa thermodynamic ke 1470 ℃~1728 ℃ (tlas'a khatello e tloaelehileng). β Cristobalite ke karolo ea eona ea mocheso o phahameng, empa e ka bolokoa ka mokhoa o tsitsitseng ho ea mocheso o tlase haholo ho fihlela phetoho ea mofuta oa phetoho e etsahala hoo e ka bang 250 ℃ α Cristobalite. Le hoja cristobalite e ka khabisoa ho tloha ho SiO2 melt sebakeng sa eona sa thermodynamic stability, boholo ba cristobalite ka tlhaho bo thehoa tlas'a maemo a tsitsitseng. Ka mohlala, diatomite e fetoha cristobalite chert kapa microcrystalline opal (opal CT, opal C) nakong ea diagenesis, 'me mekhahlelo ea bona e meholo ea liminerale ke α Cristobalite), eo mocheso oa eona oa phetoho o leng sebakeng se tsitsitseng sa quartz; Tlas'a boemo ba granulite facies metamorphism, cristobalite precipitated ho tloha morui Na Al Si melt, e ne e le teng ka garnet e le ho kenyelletsoa le ho phela hammoho le albite, ho etsa boemo ba mocheso le khatello ea 800 ℃, 01GPa, hape sebakeng se tsitsitseng sa quartz. Ho phaella moo, cristobalite e nang le metastable e boetse e thehoa linthong tse ngata tse se nang tšepe nakong ea phekolo ea mocheso, 'me mocheso oa sebopeho o sebakeng sa thermodynamic stability zone ea tridymite.
Mokhoa oa ho theha
Diatomite e fetoha cristobalite ho 900 ℃ ~ 1300 ℃; Opal e fetoha cristobalite ho 1200 ℃; Quartz e boetse e thehoa kaolinite ka 1260 ℃; The synthetic MCM-41 mesoporous SiO2 molecular sieve e ile ea fetoloa cristobalite ka 1000 ℃. Metastable cristobalite e boetse e thehoa lits'ebetsong tse ling tse kang sintering ea ceramic le mullite lokisetsa. Bakeng sa tlhaloso ea mokhoa oa ho etsa metastable oa cristobalite, ho lumeloa hore ke mokhoa o sa tsitsang oa thermodynamic, haholo-holo o laoloang ke mokhoa oa ho itšoara ka kinetics. Ho ea ka mokhoa oa ho theha metastable ea cristobalite e boletsoeng ka holimo, hoo e ka bang ka tumellano ho lumeloa hore cristobalite e fetoloa ho tloha ho amorphous SiO2, esita le ts'ebetsong ea phekolo ea mocheso oa kaolinite, ho lokisoa ha mullite le sintering ea ceramic, cristobalite e boetse e fetoloa ho tloha SiO2 ea amorphous.
Morero
Ho tloha tlhahisong ea indasteri lilemong tsa bo-1940, lihlahisoa tse ntšo tsa carbon e tšoeu li 'nile tsa sebelisoa haholo e le lisebelisoa tse matlafatsang lihlahisoa tsa rabara. Ntle le moo, li ka sebelisoa le indastering ea meriana, chefo e bolaeang likokoanyana, enke, pente, pente, sesepa sa meno, pampiri, lijo, fepa, litlolo, libeteri le liindasteri tse ling.
Mokhoa oa lik'hemik'hale oa carbon black black ka mokhoa oa tlhahiso ke SiO2nH2O. Kaha tšebeliso ea eona e tšoana le ea carbon black le e tšoeu, e bitsoa white carbon black. Ho ea ka mekhoa e fapaneng ea tlhahiso, carbon black black e ka aroloa ka carbon black black (precipitated hydrated silica) le fumed white carbon black (fumed silica). Lihlahisoa tse peli li na le mekhoa e fapaneng ea tlhahiso, thepa le tšebeliso. Mokhoa oa khase ea khase haholo-holo o sebelisa silicon tetrachloride le silicon dioxide e fumanoang ka ho tuka ha moea. Likaroloana li ntle, 'me boholo ba likaroloana tse bohareng bo ka ba tlase ho li-microns tse 5. Mokhoa oa pula ke ho fokotsa silica ka ho eketsa sulfuric acid ho sodium silicate. Boholo ba likaroloana tse bohareng bo ka bang 7-12 microns. Silika e nang le mosi e theko e boima mme ha e bonolo ho monya mongobo, kahoo hangata e sebelisoa e le ntho ea ho roala liphahlo.
Tharollo ea khalase ea metsi ea mokhoa oa nitric acid e sebetsana le asiti ea nitric ho hlahisa silicon dioxide, e ntan'o lokisoa ka har'a silicon dioxide ea boemo ba elektroniki ka ho hlatsuoa, ho qoelisoa, ho hlatsuoa ha metsi le ho felloa ke metsi.
Nako ea poso: Nov-17-2022